Abstract

Flexible transparent conductive films of micropatterned carbon nanotube networks are studied in this thesis. Plasma etching through a contact mask was used to form hydrophilic micropatterns on the surface of polyethylene terephthalate foils, which enabled the selective deposition of single-wall carbon nanotubes from their aqueous dispersions by simple dip-coating. A higher density grid-type pattern was used in conjunction with a highly concentrated ink to create transparent conductive films with sheet resistances below 10 kΩ/◻️ on the mechanically flexible polymer, which was then found suitable for capacitive touch screen applications. To confirm the conduction process in the films is due to the percolation, also a lower density line pattern was made and coated using a dispersion of lower concentration.

Yksiseinäisistä hiilinanoputkista valmistetut mikrokuvioidut läpinäkyvät johtavat kalvot plasma käsitellyllä polyetyleenitereftalaatti pinnalla

Tiivistelmä

Tämän kandintyön tutkimuskohde on mikrokuvioiduista hiilinanoputkiverkostoista koostuvat läpinäkyvät johtavat kalvot (transparent conductive film, TCF). Hydrofiilisen mikrokuvion muodostamiseen polyetyleenitereftalaattikalvon pinnalle käytettiin plasmaetsausta, mikä mahdollisti selektiivisen hiilinanoputkien päällystyksen vesipohjaisista dispersioista yksinkertaisella kastamismenetelmällä. Tiiviimpi ristikkomainen kuvio käytettynä korkeamman pitoisuuden dispersion kanssa sai aikaa kalvoja, joiden pintavastus oli parhaimmillaan alle 10 kΩ/◻ mekaanisesti taipuisan polymeerin päällä. Tällaisen kalvon todettiin olevan sopiva kapasitiivisiin kosketusnäyttösovelluksiin. Jotta johtavuus kalvoissa voitaisiin liittää perkolaatioon, tehtiin myös kalvoja harvemmalla viivakuviolla käyttäen matalamman pitoisuuden dispersiota.